Durobit EF Latex Rubber Liquid Membrane
a water based, latex emulsion waterproofing membrane. It has been tested by CSIRO (report 2947) and meets the criteria of AS4858:2004 Wet Area Membranes. It is an elastomeric, environmentally friendly membrane designed for both internal and external application. It cures to form a durable, odourless, impervious, seamless membrane that resists re-emulsifying after it has fully even if immersed in water. It does not stain grout or tiles and has excellent resistance to hydrostatic pressure.
It has been formulated for most waterproofing applications requiring long term waterproofing and meets the criteria of AS4858:2004 Wet Area Membranes and Contact With Drinking Water Test AS/NZS4020:2002 making it ideal for:
Shower Recesses & wet areas,
Tiled or topped: Decks, Terraces, balconies, podiums, roofs.
Tanks and immersed conditions.
It is suitable for suitably primed: Concrete, cement, cement render, block work, brick, masonry, FC sheeting and CFC sheeting, plaster board and timber, plywood and particle board (if primed with Primeseal) and metal (if primed with a metal primer). Note: We do not regard particle board as a suitable substrate for wet areas and if possible should be replaced or covered with CFC sheeting - particularly in shower recesses. If covered we recommend that the particle board be coated with 2 coats of Primeseal and joins and corners sealed with a polyurethane sealant prior to laying the CFC sheeting.
It may be applied to slightly damp surfaces but the product will not fully cure is the surface remains damp. This process takes longer than if the surface was allowed to dry before application. The surface must dry before the membrane can dry. Freedom from surface water, continual dampness is essential.
The information contained in this product data sheet is typical but does not constitute a full specification as conditions and specific requirements may vary from project to project. The instructions should be considered as a minimum requirement but the applicator or contractor must use their skill, knowledge and experience to carry out additional works as may be necessary to meet the requirements of the project. Specification for specific projects should be sought from the Company in writing.
it is not designed for long term direct exposure to UV and should be tiled, topped or painted. It is not designed as a trafficable membrane although infrequent maintenance foot-traffic would be acceptable.
Benefits and Advantages
It is a versatile membrane suitable for many demanding waterproofing applications:
It meets the criteria of AS4858:2004 and is applied in accordance with AS3740.
Suitable for contact with drinking water.
Formulated for wet area and under tile applications.
Does not re emulsify after proper curing.
Tough, durable and flexible.
Compatible with most tile adhesives.
Easy to apply.
Will not stain grout or tiles.
Precautions in Use
The product is considered safe to use if used correctly, as intended and proper industrial hygiene and practices are used. Always observe safety precautions. Priming and Surface preparation: Good preparation is essential. Surfaces must be sound, stable, dry, clean and free of dust, loose, flaking, friable material and substances that may diminish adhesion.
Surfaces should be suitably primed with Primeseal applied at no less than 1 litre per 4m2 and allowed to dry. Primeseal must be used for roof and exposed areas, timber and particle board surfaces, bitumen or
where there is a risk of entrapped moisture in the substrate which may cause the membrane to bubble.
Priming is ad equate if the surface has a solid off-white appearance. Particle board and bitumen surfaces should primed with 2 coats of Primeseal. Alternative primers such as WB Primer. may be used in non-exposed areas and where the moisture content of the surface is very low applied at no less than 1 litre per 4 sqm. Excessively porous, friable and dusty surfaces may require an additional priming coat. Please refer to the product data sheets of the stated primers.
Prime as required.
Apply an adequate flexible polyurethane sealant, in accordance the manufacture's instruction and tool off to form a solid, coved or 45 degree fillet extending at least 10mm on to the adjacent surfaces. Apply the Wrimco membrane directly over the sealant and on the adjacent surfaces.
For Additional waterproofing protection the following additional steps should be taken
Lay a strip of Seal leak tape (stick-stick, butyl mastic waterproofing membrane with a polyester backed reinforcing fabric) over the cured polyurethane sealant (as described above) pressing it firmly on the surface. Apply the Wrimco membrane directly over the tape and on the adjacent surfaces.
Joins, Gaps and Cracks
Joins, gaps and cracks should be suitably filled and sealed with an appropriate elastomeric sealant, preferably a polyurethane sealant, and allowed to cure.
Recommendation: The movement of small cracks should not be underestimated and should be at least covered with a flexible polyurethane sealant or additional coats of membrane.
Large or Live Cracks
Large cracks should be routed out to form a 'V' and then filled and sealed with a polyurethane waterproof joint sealant as per the manufacturer's instructions. The sealant should be finished slightly proud of the surface and allowed to cure.
After priming, as required, lay a strip of Seal leak tape over the join or crack pressing it firmly on to the substrate. The membrane is then applied directly to the Wrimco Flashing Tape and extending at least 75mm on to the adjacent surfaces.
If Seal leak tapeis not used then a suitable bond breaker tape (such as duct tape) at least 48mm wide should be laid over the join or crack and apply a fully reinforced Wrimco membrane consisting of a base coat of membrane in to which the reinforcing fabric is embedded, a saturating coat of the membrane ensuring that the fabric is entirely saturated and covered and then allowed to cure. At least one or two further coats are applied as per the membrane's Product Data Sheet extending at least 75mm on to the adjacent surfaces.
Joins - Particularly in CFC Sheeting and Timber Sheeting
Ideally the sides of the sheets should be fully coated with a flexible polyurethane waterproof joint sealant prior to butting the sheets together.
If not, the joins should be suitably filled and sealed with an appropriate elastomeric polyurethane waterproof sealant and finished flush with or preferably slightly proud of the surface and allowed to cure.
After priming, as required, lay a strip of Seal leak tape over the join, pressing it firmly on to the substrate. The membrane is then as described under 'Large or Live Cracks'.
If the Seal leak tape is not used then follow the procedure as described under 'Large or Live Cracks'.
Waste Outlets, Penetrations and Angles
Waste Outlets: Floor wastes and puddle flanges should be rebated in to the floor to allow water to readily drain. Gaps and perimeters should be sealed with a polyurethane sealant.
Plastic or metal angles: Where required by the Building Code such as internal hobs and exterior door barriers and also plastic corner angels under wall boards, they should be securely embedded in to a continuous, gap free bed of a polyurethane sealant / mastic.
Stir well. Apply by brush, roller, soft broom or spray.
Apply in a minimum of two coats. To perform correctly the dry film thickness of the membrane must be at least 1mm to 1.2 mm.
Durabit EF is suitable for use with a reinforcing fabric and Seal leak tape.
In areas such as corners and over joins and cracks the membrane should be used in conjunction with a reinforcing fabric or fibreglass matting. This application consists of applying a base coat in to which the reinforcing fabric is laid followed by the application of a saturating coat ensuring that the product is worked well in to the fabric and that no wrinkles or bubbles are present and that fabric is entirely saturated and covered with product. Allow to cure. Apply one or two further coats of products.
The stated average coverage rate may vary depending upon type, condition, porosity, texture of the surface and application technique.
Unreinforced: Minimum 1.5 litres per sq.m., i.e 0.75 litres per m2 per coat. A 15 litre pail will cover 10 sq.m. for 2 coats.
Reinforced: Minimum: 2.0 litres per m2.
The dry film thickness fo the membrane must be at least 1mm.
Minimum 1 litre per 4m2.
It is available in white, grey, blue, black. Special colours available upon request but minimum orders will apply.
Drying and Curing
Drying and curing of the product is affected by type, dryness and porosity of the surface, temperature, humidity, ventilation, climate conditions and application technique and therefore drying and curing can only be given as a guide.
It is a fast drying water based product. Expected curing at 25 C at 50% RH: Touch dry - 4 to 6 hours per coat. Set - 12 hours. Full cure 36 to 72 hours per coat. Ensure membrane is fully cured before tiling or topping.
Store in cool, dry area. Product is not flammable. Do not allow to freeze. Shelf life - about 12 months. Available in 1, 4, and 15 litre pails.
Wet spills can be cleaned with water, but spills should be avoided.
Tiling, Topping or Top Coating
It is compatible with most tile adhesives and 3:1 sand:cement beds.
Ideally the beds should be sealed / waterproofed to prevent the bed absorbing and holding water. Selection of the tile adhesive should be compatible with the flexibility of the substrate. Two pack adhesives systems are preferred. Tiling must be done in accordance with AS3958.1-1991 and adequate expansions joints installed.
Safety & Precautions
It is user friendly and safe to use if used correctly as intended. Nevertheless, protect eyes and skin and observe the safety precautions on the can and data sheet. For full safety data refer to the products Material Safety Data Sheet. Observe precautions as per label.
Tests and Technical Data
It complies with AS4858:2004 Wet Area Membranes as tested by the CSIRO Test Report 2947 with a Class III High Extensibility classification. It complies with AS/NZ 4020:2002 Contact With Drinking Water. Application temperature range: 10 to 35 C
Tensile Bond: 2N/mm after 14 days.
Moisture Vapour Transmission: 0.26 g/sq.m./24 hours
Elongation: > 300% (Class 111 Extensibility)